C2103M

Description

C2103M is a Pd/Ag Conductor paste which exhibits high density, high reliability and good fine line definition, (6 mil lines and spaces). It fires to a smooth surface and is mechanically durable and chemically resistant. Conductivity, leach resistance, and resistance to silver migration are exceptional. Due to these characteristics pastes such as C2103M are frequently preferred material for fuel level sensor applications.

Key Features

Excellent solderability and leach resistance Exceptional silver migration resistance Smooth fired surface

Metal

AgPd

Viscosity

180 – 240 Kcps Brookfield HBTSC4 – 14 spindle, 6R utility cup at 10 rpm, 25 °C

Coverage

84 cm²/g at 12 μm fired film thickness

Coverage

84 cm²/g at 12 μm fired film thickness

Storage and Paste Preparation

Store in a dry condition at 5 – 25 °C,

Warranty

6 months

Printing Parameters

280 – 325 mesh stainless steel screen 0.5 mil emulsion, 1.1 mil wire Let the print level at room temperature for 10 minutes before drying

Printing Speed

up to 6 in/sec

Drying Temperature

150 °C for 10 minutes_x000D_

Process Temperature (TDS)

850 °C peak for 10 minutes,Total cycle time 30 – 60 minutes

Film Thickness

Wet: 34 – 38 µm Dried: 18 – 22 µm Fired: 10 – 13 µm