- Paste Type: Conductor
- Application Method: Screen Printing
- Substrate: Alumina
- Metal: AgPd
- Application: FLS/Potentiometers
- Description: C2103M is a Pd/Ag Conductor paste which exhibits high density, high reliability and good fine line definition, (6 mil lines and spaces). It fires to a smooth surface and is mechanically durable and chemically resistant. Conductivity, leach resistance, and resistance to silver migration are exceptional. Due to these characteristics pastes such as C2103M are frequently preferred material for fuel level sensor applications.
- Key features: Excellent solderability and leach resistance
Exceptional silver migration resistance
Smooth fired surface
- Printing Parameters: 280 – 325 mesh stainless steel screen
0.5 mil emulsion, 1.1 mil wire
Let the print level at room temperature for 10 minutes before
drying
- Process Temperature: 850 °C peak for 10 minutes,Total cycle time 30 – 60 minutes
- Film Thickness : Wet: 34 – 38 µm
Dried: 18 – 22 µm
Fired: 10 – 13 µm
- Viscosity: 180 – 240 Kcps Brookfield HBTSC4 – 14 spindle, 6R utility cup at 10 rpm, 25 °C
- Conductivity: ≤ 50 milliohms/square at 12 um fired film thickness
- Solids: 83.0 ± 1.0 %
- Resistivity (Ohm/sq.): ≤ 50 mΩ/ at 12 μm fired film thickness